Test Report
 

ALL TEST BASED ON IS 15298:2002
THE SAMPLE WAS CONDITIONED FOR 48 HOURS
UNDER LAB ENVIRONMENT TEMPERATURE
RELATIVE HUMIDITY
20+/-2 C

65+/-5%

S.NO.

TEST NAME

VALUE REQUIRED

1

 

PEEL STRENGTH BETWEEN UPPER

AND SOLE.

4.3N/MM

4.0N/MM

 

2 ABRASION RESISTANCE TEST

87mm cube

volume loss

250mm cube
maximum

3

HARDNESS (SHORE A) 60 SHORE A  
4

TENSILE STRENGTH (KG/CM CUBE)

249

210(MIN)

5

% ELONGATION

53 45-75
6 TONGUE TEAR (KG/CM CUBE)

76

40(MIN)

7

BALLY FLEXING UP TO 1LAC CYCLES

NO DAMAGE 1 LAC MIN
8 ROSS FLEX (INITIAL CRACK)
60000 CYCLES

NO CRACK

60000 CYCLES

9

ROSS FLEX (CUT GROWTH)
120000 CYCLES

100% CUT GROWTH

400% MAX

10

SPECIFIC GRAVITY

1.3

1.3 MAX

11 ELECTRICAL RESISTANCE

20 KV

20 KV

 